BSO crystals «In Stock»

Bismuth silicone oxide (Bi12SiO20, BSO) crystals are highly efficient photoconductors with a low dark conductivity, that allows a build-up of large photo-induced space-charges. Tremendous photoconductivity and electro-optic properties make BSO crystals attractive in a range of applications: spatial light modulators, optical switches, phase conjugation mixers. BSO crystals are grown by modified Czochralski method and available in up to 3‘‘ diameter aperture size.

Crystals can be supplied with ITO coatings on request.

Request custom View catalog
Order your item

Items can be filtered by multiple words e.g., "uvfs 1064"

SPECIFICATION SKU PRICE Qty. of stock QUANTITY
10x10 mm; 1 mm; [110]; 40/20 S/D; <λ/4 at 632,8 nm; >85 %; +/-0,2 mm; ±0,2 mm; <30 arcsec; uncoated
12054
240 €
5
15x15 mm; 1 mm; [110]; 40/20 S/D; <λ/4 at 632,8 nm; >85 %; +/-0,2 mm; ±0,2 mm; <30 arcsec; uncoated
12138
Request
1
10x10 mm; 20 mm; [001]; 40-20 S-D; λ@632,8 nm; >85 %; ±0,2 mm; ±0,02 mm; <3 arcmin; uncoated
16981
Request
1
20x20 mm; 1,5 mm; [100]; 40-20 S-D; <λ/4 at 632,8 nm; >85 %; +/-0,2 mm; ±0,2 mm; <30 arcsec; uncoated
20002
490 €
>5
25x25 mm; 1,0 mm; [110]; 40-20 S-D; <λ/4 at 632,8 nm; >85 %; +/-0,2 mm; +0,2/-0 mm; <30 arcsec; S1: uncoated&#x0D; S2: ITO+AR, Tmax@532nm, resistivity 500-1000 Ohms/sq, ITO coating mask 23x23mm aperture&#x0D; AR coating mask 23x21mm aperture
27782
570 €
1
12x12mm; 1 mm; [111]; 40-20 S-D; λ/2 at 632,8 mm; >85 %; +/-0,2 mm; ±0,2 mm; <3arcmin; uncoated
29097
Request
>5
12x12 mm; 5 mm; [111]; 40-20 S-D; λ/2 at 632,8 mm; >85 %; +/-0,2 mm; ±0,2 mm; <3arcmin; uncoated
29098
Request
3
12x12 mm; 5 mm; <100>; 40-20 S-D; λ/2 at 632,8 mm; >85 %; +/-0,2 mm; ±0,2 mm; <3arcmin; uncoated
29099
Request
1
12x12mm; 1 mm; <100>; 40-20 S-D; λ/2 at 632,8 mm; >85 %; +/-0,2 mm; ±0,2 mm; <3arcmin; uncoated
29100
Request
>5
12x12mm; 1 mm; <210>; 40-20 S-D; λ/2 at 632,8 mm; >85 %; +/-0,2 mm; ±0,2 mm; <3arcmin; uncoated
29101
Request
>5
12x12 mm; 5 mm; <210>; 40-20 S-D; λ/2 at 632,8 mm; >85 %; +/-0,2 mm; ±0,2 mm; <3arcmin; uncoated
29102
Request
3
2,7x2,7 mm; 1,4 mm; [110]; 40-20 S-D; <λ/4 at 632,8 nm; >85 %; +/-0,1 mm; +/-0,1 mm; ≤3 arcmin; uncoated
29380
Request
>5
2,7x2,7 mm; 1,4 mm; [110]; 40-20 S-D; <λ/4 at 632,8 nm; >85 %; +/-0,1 mm; +/-0,1 mm; ≤3 arcmin; uncoated
29967
Request
>5
25x25 mm; 1,0 mm; [110]; 40-20 S-D; <λ/4 at 632,8 nm; >85 %; +/-0,2 mm; +0,2/-0 mm; <30 arcsec; uncoated
31028
Request
>5
2,7x2,7 mm; 3 mm; [210]; Aptrupėjimai, taškai; <λ/4 at 632,8 nm; >85 %; +/-0,1 mm; +/-0,1 mm; ≤3 arcmin; uncoated
31613
Request
3
25x25 mm; 5 mm; [110]; 40/20 S/D; <λ/4 at 632,8 nm; >85 %; +/-0,2 mm; ±0,2 mm; <30 arcsec; uncoated
33272
Request
2
12x12 mm; 5 mm; <110>+/-2%; 40-20 S-D; λ/2 at 632,8 mm; >85 %; +/-0,2 mm; ±0,2 mm; <3arcmin; uncoated
33273
Request
3
12 x 12 mm; 1,1 mm; [110]; 40/20 S/D; <λ/4 at 632,8 nm; >85 %; +/-0,2 mm; ±0,2 mm; <30 arcsec; uncoated
33637
Request
1
20x20 mm; 1,0 mm; [110]; 40/20 S/D; <λ/4 at 632,8 nm; >85 %; +/-0,2 mm; ±0,2 mm; <30 arcsec; uncoated
6880
490 €
2
20x20 mm; 1,0 mm; [100]; 40/20 S/D; <λ/4 at 632,8 nm; >85 %; +/-0,2 mm; ±0,2 mm; <30 arcsec; uncoated
6881
490 €
2