Yb:KGW crystals «In Stock»
Yb3+:KGW crystals possess a large gain bandwidth that enables them to obtain <100 fs pulse duration in the mode-locked regime of operation. Compared with other ytterbium-doped gain media with a similarly large gain bandwidth, ytterbium-doped tungstate has fairly high emission cross-sections. The ytterbium doping concentration in Yb:KGW crystals can be up to 5 at. % without a significant quenching. Thermal conductivity of common double tungstates is in the range of 3–4 Wm-1K-1. Yb:KGW crystals exhibit a small quantum defect and it is possible to operate with a quantum defect well below ~4-5%.
Request custom
View catalog
Order your item
Items can be filtered by multiple words e.g., "uvfs 1064"
SPECIFICATION
SKU
PRICE
Qty. of stock
QUANTITY
Yb:KGW; 1%; Ng cut; 1(Nm)x10(Np) mm; 10 mm; wedged (5°)/wedged (5°); AR@1010-1060(<0,2%)+AR@975-985(<0,5%) AOI=0deg; AR@1010-1060(<0,2%)+AR@975-985(<0,5%) AOI=0deg
17452
Request
1
Yb:KGW; 1,5%; Ng cut; 1(Nm)x10(Np) mm; 10 mm; wedged (5°)/wedged (5°); AR@1010-1060(<0,2%)+AR@975-985(<0,5%) AOI=0deg; AR@1010-1060(<0,2%)+AR@975-985(<0,5%) AOI=0deg
17454
Request
1
Yb:KGW; 3,8%; Ng cut; 1,0(Np)x4(Nm) mm; 2 mm; Right-angle cut/wedge (2°); +0/-0,1 mm; +/-0,2 mm; > 85 %; 10-5 S-D; < λ/10; < 30 arcsec; AR(R<0,3%)@940 - 1050nm, AOI=0deg; AR(R<0,3%)@940 - 1050nm, AOI=0deg
28362
Request
3
Yb:KGW; 3,8%; Ng cut; 1,5(Np)x4(Nm) mm; 2 mm; Right-angle cut/wedge (2°); +0/-0,1 mm; +/-0,2 mm; > 85 %; 10-5 S-D; < λ/10; < 30 arcsec; AR(R<0,3%)@940 - 1050nm, AOI=0deg; AR(R<0,3%)@940 - 1050nm, AOI=0deg
28363
Request
1
Yb:KGW; 3,8%; Ng cut; 1,0(Np)x4(Nm) mm; 2 mm; Right-angle cut/wedge (2°), as marked in drawing; +0/-0,1 mm; +/-0,2 mm; > 85 %; 10-5 S-D; < λ/10; < 30 arcsec; AR(R<0,3%)@940 - 1050nm, AOI=0deg; AR(R<0,3%)@940 - 1050nm, AOI=0deg
30544
Request
2
; 5%; Ng-cut; 3x3 mm; 2 mm; Right-angle cut; +0/-0,1 mm; ±0,1 mm; >90%; 10-5 S-D; <λ/10; <10 arcsec; <0,1 mm at 45˚; AR/AR@970-1070 nm; AR/AR@970-1070 nm; >10 J/cm2@1040 nm, 10 ns; AR/AR@970-1070 nm
7061
590 €
2
1
/1