Nd:YAG crystals «In Stock»
Nd3+:YAG crystal is the most widely used solid-state laser material. These crystals are characterized by relatively small gain bandwidth, which allows achieving a high gain efficiency and a relatively low lasing threshold. Nd:YAG crystals feature excellent thermal and mechanical properties. Nd:YAG of high optical quality and large diameter can be grown.
Request custom
View catalog
Order your item
Items can be filtered by multiple words e.g., "uvfs 1064"
SPECIFICATION
SKU
PRICE
Qty. of stock
QUANTITY
11122
Request
>5
⌀3 mm; 6,5mm+/-0,1mm; [111]; 1%; +0/-0,1 mm; 20/10SD; <λ/8; <10arcsec; AOI 0˚ AR(R<0,15%)@1064nm+R<1%@808nm; AOI 0˚ AR(R<0,15%)@1064nm+R<1%@808nm; high LIDT >10J/cm2, 10ns
1680
180 €
1
3x3 mm; 10 mm; 0,8%; +0/-0,1 mm; 20/10SD; <λ/8; <20 arcsec; AOI 0˚; R=40%@1064nm (on YAG); HR@1064+HT@808, (on Cr:YAG)
18227
Request
1
3x3 mm; 8 mm; [111]; 1,1%; Right-angle cut; +0/-0,1 mm; ±0,1 mm; >90%; 10-5 S-D; <λ/8; <λ/8 at 632,8 nm; <20 arcsec; <10 arcmin; <0,1 mm at 45˚; HR(R>99,5%)@1064 nm+HT(T>95%)@808 nm; AOI 0˚ PR(R=50%+/-2%)@1064nm+R<5%@808nm (on Cr:YAG); >10 J/cm2@1064 nm,
18230
Request
>5
3x3 mm; 8,3 mm; [111]; 1,1%; Right-angle cut; +0/-0,1 mm; ±0,1 mm; >90%; 10-5 S-D; <λ/8; <λ/8 at 632,8 nm; <20 arcsec; <10 arcmin; <0,1 mm at 45˚; HR(R>99,5%)@1064 nm+HT(T>95%)@808 nm; AOI 0˚ T=52%+/-2%@1064nm+HR@532nm (on Cr:YAG); >10 J/cm2@1064 nm, 10 n
18231
Request
1
19940
Request
2
⌀2,5 mm; 1,0mm+/-0,1mm(Nd:YAG)+0,3mm+/-0,05mm(Cr:YAG); Nd:YAG[111]+Cr:YAG[110]!!; 1,3%; +0/-0,1 mm; 20/10SD; <λ/8; <10arcsec; AOI 0˚; R>99,9%@1064nm , T>98%@808nm (on Nd:YAG); AOI 0˚ PR(R=50%)@1064nm+R<5%@808nm (on Cr:YAG); high LIDT >10J/cm2, 10ns
2412
300 €
1
⌀2,5 mm; 1,0mm+/-0,1mm(Nd:YAG)+0,3mm+/-0,05mm(Cr:YAG); Nd:YAG[111]+Cr:YAG[110]!!; 1,3%; +0/-0,1 mm; 20/10SD; <λ/8; <10arcsec; AOI 0˚; R>99,9%@1064nm , T>98%@808nm (on Nd:YAG); AOI 0˚ PR(R=30%+/-2%)@1064nm+R<5%@808nm (on Cr:YAG); high LIDT >10J/cm2, 10ns
2413
300 €
1
⌀2,5 mm; 6,5mm+/-0,1mm(Nd:YAG)+1,25mm+/-0,2mm(Cr:YAG); Nd:YAG[111]+Cr:YAG[110]!!; 1%; +0/-0,1 mm; 20/10SD; <λ/8; <10arcsec; AOI 0˚; R>99,9%@1064nm , T>98%@808nm (on Nd:YAG); AOI 0˚ PR(R=50%+/-2%)@1064nm+R<5%@808nm (on Cr:YAG); high LIDT >10J/cm2, 10ns
2415
300 €
1
⌀2,5 mm; 0,5mm+/-0,1mm(Nd:YAG)+0,5mm+/-0,2mm(Cr:YAG); Nd:YAG[111]+Cr:YAG[110]!!; 1%; +0/-0,1 mm; 20/10SD; <λ/8; <10arcsec; AOI 0˚; R>99,9%@1064nm , T>98%@808nm (on Nd:YAG); AOI 0˚ PR(R=78,5%+/-1%)@1064nm+R<5%@808nm (on Cr:YAG); high LIDT >10J/cm2, 10ns
2416
300 €
1
29804
Request
1
29805
Request
1
⌀2,5 mm; 1,0mm+/-0,1mm(Nd:YAG)+0,3mm+/-0,05mm(Cr:YAG); Nd:YAG[111]+Cr:YAG[110]!!; 1,3%; +0/-0,1 mm; S1: 20-50 S-D; S2: 40-20 S-D; <λ/8; <10arcsec; AOI 0˚; R>99,9%@1064nm , T>98%@808nm (on Nd:YAG); AOI 0˚ PR(R=50%)@1064nm+R<5%@808nm (on Cr:YAG); high LIDT
33541
Request
1
5897
Request
1
1
/1
Show all